Secant modulus of elasticity of concrete at 28 days according to the type of aggregates used, Ecm – 3.1.3
Approximate values for the secant modulus of elasticity of concrete Ecm at 28 days are given in table below for concretes with quartzite aggregates. For limestone and sandstone aggregates the value should be reduced by 10% and 30% respectively. For basalt aggregates the value should be increased by 20%.
The following application calculates the modulus of elasticity Ecm from your inputs.
| Strength classes for concrete | ||||||||||||||
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
| fck (MPa) | 12 | 16 | 20 | 25 | 30 | 35 | 40 | 45 | 50 | 55 | 60 | 70 | 80 | 90 |
| fck,cube (MPa) | 15 | 20 | 25 | 30 | 37 | 45 | 50 | 55 | 60 | 67 | 75 | 85 | 95 | 105 |
| fcm (MPa) | 20 | 24 | 28 | 33 | 38 | 43 | 48 | 53 | 58 | 63 | 68 | 78 | 88 | 98 |
| fctm (MPa) | 1,6 | 1,9 | 2,2 | 2,6 | 2,9 | 3,2 | 3,5 | 3,8 | 4,1 | 4,2 | 4,4 | 4,6 | 4,8 | 5 |
| fctk,0,05 (MPa) | 1,1 | 1,3 | 1,5 | 1,8 | 2 | 2,2 | 2,5 | 2,7 | 2,9 | 3 | 3,1 | 3,2 | 3,4 | 3,5 |
| fctk,0,95 (MPa) | 2 | 2,5 | 2,9 | 3,3 | 3,8 | 4,2 | 4,6 | 4,9 | 5,3 | 5,5 | 5,7 | 6 | 6,3 | 6,6 |
| Ecm (GPa) | 27 | 29 | 30 | 31 | 33 | 34 | 35 | 36 | 37 | 38 | 39 | 41 | 42 | 44 |
| εc1 (‰) | 1,8 | 1,9 | 2 | 2,1 | 2,2 | 2,25 | 2,3 | 2,4 | 2,45 | 2,5 | 2,6 | 2,7 | 2,8 | 2,8 |
| εcu1 (‰) | 3,5 | 3,2 | 3 | 2,8 | 2,8 | 2,8 | ||||||||
| εc2 (‰) | 2 | 2,2 | 2,3 | 2,4 | 2,5 | 2,6 | ||||||||
| εcu2 (‰) | 3,5 | 3,1 | 2,9 | 2,7 | 2,6 | 2,6 | ||||||||
| n | 2 | 1,75 | 1,6 | 1,45 | 1,4 | 1,4 | ||||||||
| εc3 (‰) | 1,75 | 1,8 | 1,9 | 2 | 2,2 | 2,3 | ||||||||
| εcu3 (‰) | 3,5 | 3,1 | 2,9 | 2,7 | 2,6 | 2,6 | ||||||||